The thickness/viscosity of the resin would be a concern. I would think if you had it more "watery" than "paste" like, you would get a very porous structure when you fire the print and the resin burns out. That or you would need to play with particle size of whatever material to alleviate that issue.
But I think it's more or less creating a weak bond f whatever material and photocurable resin to create the desired structure, once its done printing, you put it in a kiln and have all the resin burn out all the while bonding whatever material.Statistics: Posted by AndersonTa — Wed Apr 16, 2014 2:47 pm
]]>