Re: New UV Resin Supplier
It sound nice.
Would you please put some picture of samples printed by this resin and casting results?
Thanks
Would you please put some picture of samples printed by this resin and casting results?
Thanks
- Tue Jun 23, 2015 5:15 pm
- Forum: Hardware showcase / Build Logs
- Topic: Getting prints to stick to build plate
- Replies: 6
- Views: 17463
Re: Getting prints to stick to build plate
Hi Man This problem can be caused by low ratio adherence between the build plate and the VAT. for best printing this ratio will be more than 100.So you should use a metal with high adherence like Aluminum with a good polish surface as a build plate and use Teflon VAT like with super low adherence. ...
- Tue Jun 23, 2015 12:43 pm
- Forum: Hardware showcase / Build Logs
- Topic: Getting prints to stick to build plate
- Replies: 6
- Views: 17463
Re: Getting prints to stick to build plate
Hi Man
This problem can be caused by low ratio adherence between the build plate and the VAT.
for best printing this ratio will be more than 100.So you should use a metal with high adherence like Aluminum with a good polish surface as a build plate and use Teflon VAT like with super low adherence.
This problem can be caused by low ratio adherence between the build plate and the VAT.
for best printing this ratio will be more than 100.So you should use a metal with high adherence like Aluminum with a good polish surface as a build plate and use Teflon VAT like with super low adherence.
- Sat Jun 20, 2015 5:30 pm
- Forum: Resins
- Topic: Resins For Investment Casting
- Replies: 57
- Views: 128630
Re: Resins For Investment Casting
Hi Luke
Have you tested the ROR ?
It seem interesting
wait for feedback for group.
Have you tested the ROR ?
It seem interesting
wait for feedback for group.