Ted talk here:
http://www.ted.com/talks/joe_desimone_w ... r#t-285853
with one of the inventor Jo DeSimone, and live demo.
Search found 82 matches
- Thu Mar 19, 2015 3:01 pm
- Forum: Commerical Machines
- Topic: Carbon 3D
- Replies: 243
- Views: 558926
- Thu Mar 19, 2015 5:20 am
- Forum: Commerical Machines
- Topic: Carbon 3D
- Replies: 243
- Views: 558926
- Tue Mar 17, 2015 3:56 pm
- Forum: Commerical Machines
- Topic: Carbon 3D
- Replies: 243
- Views: 558926
Re: Carbon 3D
if the minimum order qty is huge amount of money, let's start a small kickstarter project so we can all pledge the money to buy this heavenly film !
count me in.
count me in.
- Wed Mar 11, 2015 1:37 pm
- Forum: Resins
- Topic: Can we use salt water on a bottom up machine ?
- Replies: 4
- Views: 14866
Re: Can we use salt water on a bottom up machine ?
ok, someone has tried it here with glycerin: http://b9creator.com/forum/viewtopic.php?f=18&t=1331 with limited success, but then the thread branches out but the link is invalid, they're talking about using a thin transparent film between the glycerin and resin, with a certain tension i guess, to...
- Wed Mar 11, 2015 7:51 am
- Forum: Resins
- Topic: Can we use salt water on a bottom up machine ?
- Replies: 4
- Views: 14866
Can we use salt water on a bottom up machine ?
I promise I searched the forum before posting :
In a bottom up setup, can we use a little layer of salt water between the vat floor and the resin ? To avoid the sticking problem..
Slap me on the fingers with a thick wooden ruler if that was already asked
In a bottom up setup, can we use a little layer of salt water between the vat floor and the resin ? To avoid the sticking problem..
Slap me on the fingers with a thick wooden ruler if that was already asked
- Sun Feb 22, 2015 1:45 pm
- Forum: Commerical Machines
- Topic: Titan1 from Kudo3d.com - first good print
- Replies: 1
- Views: 10366
Titan1 from Kudo3d.com - first good print
Hi guys, thought i'd share this one, i receive my Titan1 from Kudo3d.com 2-3 weeks ago and after some trials and errors i managed to get a couple of good prints now, pictures below, Sliced with CW (thanks Pacmanfan !) at 50 microns and antialiasing set at 3.5, printed at 100XY with Funtodo Ind Blend...
- Thu Feb 19, 2015 3:29 pm
- Forum: Hardware showcase / Build Logs
- Topic: DIY, Post-curing oven
- Replies: 3
- Views: 12980
Re: DIY, Post-curing oven
this is cool, thanks for the idea, i was thinking of building one but did not think about something so simple.
- Wed Feb 18, 2015 3:13 pm
- Forum: Buy / Sell / Trade
- Topic: Buy Teflon, FEP Film
- Replies: 23
- Views: 57484
- Fri Feb 06, 2015 7:44 am
- Forum: Hardware showcase / Build Logs
- Topic: DLP Printer, FlexVat, Germany
- Replies: 23
- Views: 62016
Re: DLP Printer, FlexVat, Germany
Thanks for sharing your experience.
Am I correct that your vat is fixed (no tilt, no movement) and your FEP film does not lay on a glass plate or anything else ?
Am I correct that your vat is fixed (no tilt, no movement) and your FEP film does not lay on a glass plate or anything else ?
- Fri Feb 06, 2015 1:05 am
- Forum: 3d Prints
- Topic: My Printer in Actione - inc Flexvat
- Replies: 44
- Views: 91329
Re: My Printer in Actione - inc Flexvat
Will definitely design a system to increase tension.
Thanks for the info on squeeze out time, clear.
You mention vat tilt, I was under the impression your vat was fixed and not tilting. The one I'm building is fixed. Can FEP work with a completely fixed vat ?
Thanks for the info on squeeze out time, clear.
You mention vat tilt, I was under the impression your vat was fixed and not tilting. The one I'm building is fixed. Can FEP work with a completely fixed vat ?